Ceramic Chip Capacitors
Multilayer chip capacitors have a low residual inductance, an excellent fre...
www.DataSheet4U.com
Ceramic Chip
Capacitors
Multilayer chip
capacitors have a low residual inductance, an excellent frequency response and minimal stray capacitance since there are no leads. These characteristics enable design to be very close to the theoretical values of the
capacitors.
NP0/C0G:
15% 10% 5% 0% -5% -10% -15% -55°C -25°C 0°C
SPECIFICATIONS:
Typical Capacitance Change vs. Temperature
OPERATING TEMPERATURE RANGE: TEMPERATURE COEFFICIENT: TEMPERATURE
VOLTAGE COEFFICIENT: DISSIPATION FACTOR: INSULATION RESISTANCE: AGEING: WITHSTANDING
VOLTAGE: TEST PARAMETERS:
25°C
50°C
75°C
100°C
125°C
CAPACITANCE TOLERANCE: OPERATING TEMPERATURE RANGE: TEMPERATURE COEFFICIENT: TEMPERATURE
VOLTAGE COEFFICIENT: DISSIPATION FACTOR:
-55°C to +125°C 0 ±30PPM/°C 0 ±30PPM/°C 0.1% MAX. >1000 ohms F or 100 G ohms, whichever is less at 25°C, VDCW. (The IR at 125°C is 10% of the value at 25°C) None >2.5 times VDCW 1MHz ± 100KHz at 1.0 ± 0.2 Vrms ≤ 100 pF, 25°C 1KHz ± 100Hz at 1.0 ± 0.2 Vrms > 100 pF, 25°C B,C,D,F,G,J,K -55°C to +125°C 0 ±15%∆°C MAX. X7R not applicable For 50 volts and 100 volts: 2.5% MAX.; For 25 volts: 3.0% MAX.; For 16 volts: 3.5% MAX.; For 10 volts: 5.0% MAX.; For 6.3 volts: 10% MAX. For values > 10µF and
voltages ≤ 10V, the D.F. is 10% MAX. >1000 ohms F or 100 G ohms, whichever is less at 25°C, VDCW. (The IR at 125°C is 10% of the value at 25°C) 2.5% per decade hour, typical >2.5 times VDCW 1KHz ± 100Hz at 1.0 ± 0.2 Vrms > 100 pF, 25°C J,K,M -55°C to +85°C 0...